Default How to resolder the panel edge strips?????

Hello solar guys,
I have a solar panel on my boat for a maintence charger about 3 ft x 1 ft, which stopped charging a while ago. I pulled the aluminum edging off the end with the output wires and found the negative wire solder joint to what looks like a ribbon accross that end of the panel had detached, so no go.
Tried to resolder with rosin core to the shiny strip after scraping it but wouldn't flow onto what I think is the shiny connection ribbon. Is it coated with something?
Or is there some trick to getting it to wet out with solder??
Pics attached but the end of it isn't really that dirty!








Attached Thumbnails
Click image for larger version

Name:	IMG_20190128_155854900.jpg
Views:	263
Size:	449.5 KB
ID:	8502   Click image for larger version

Name:	IMG_20190128_155912363.jpg
Views:	287
Size:	436.4 KB
ID:	8503   Click image for larger version

Name:	IMG_20190128_155959414.jpg
Views:	272
Size:	438.6 KB
ID:	8504   Click image for larger version

Name:	IMG_20190128_160022112.jpg
Views:	260
Size:	493.7 KB
ID:	8505  

Last edited by Daox; 01-29-19 at 07:37 AM..
Ron342 is offline   Reply With Quote
Old 01-29-19, 08:43 PM   #2
where2
DIY Geek
 
Join Date: Apr 2013
Location: Sunny Florida
Posts: 400
Thanks: 72
Thanked 83 Times in 73 Posts
Default

That's an amorphous solar panel. Techniques used are a bit different than a silicon wafer panel. My experience is with buss leads in a wafer which went well with a soldering gun.

Here's some excerpts from a patent on a methodology used to solder the buss wires...

[0005]
Without the adhesive metal layer, the adhesion of the silver layer to the AZO layer is, technically speaking, sufficient to provide good device performance with the highest current and best conversion efficiency. The biggest problem occurs during the soldering process employed to connect a buss wire to the back contact. During this soldering, the back contact is subjected to high temperature (greater than about 220° C.) and solder flux material, a potentially corrosive chemical, which causes delamination between the AZO and silver interface.


[0006]
Delamination is not solely due to poor adhesion (interface strength) between AZO and the silver layers, but due to other factors as well. The factors that affect the delamination include, in no particular order: (1) interface strength (adhesion between the AZO layer and the silver layer; (2) high temperatures applied to the back contact during soldering causing film cracks along grain boundaries; (3) the corrosive flux used during soldering; (4) a combination of high temperature during soldering and the corrosive flux reacting with the silver and causing delamination at the AZO interface; and (5) film stress mismatch between films in the back contact stack causes sever delamination and flux penetration (and corrosion) during soldering due to thermal stress, resulting in delamination at the AZO—silver interface.

If you'd like to read the entire document
https://patents.google.com/patent/US20120088327A1/en
where2 is offline   Reply With Quote
The Following User Says Thank You to where2 For This Useful Post:
Ron342 (02-04-19)
Old 02-04-19, 09:14 AM   #3
Ron342
Apprentice EcoRenovator
 
Join Date: Feb 2010
Location: Maryland
Posts: 120
Thanks: 26
Thanked 12 Times in 8 Posts
Default Resoldering Panel edges

Thanks Where 2
I read the patent - which seems to point out that putting these together is not just simple soldering - much more if its been exposed to salt air and covered with silicone caulk like mine.
Online i found some references to specialty fluxes and solders and a reference to bonding the wire to the existing flat strip(Copper?? it has a reflective finish I can't figure out) with epoxy embedded with silver dust - which i happen to have.
So I think I'll try to find the solder/flux first and then try the epoxy - its not a hi output panel but i don't even really know when if I'm down to bare surface on the ribbon strip!

Ron342 is offline   Reply With Quote
Reply


Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -5. The time now is 09:07 AM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2021, vBulletin Solutions Inc.
Ad Management by RedTyger
Inactive Reminders By Icora Web Design